Titre :
H2-induced copper and silver nanoparticle precipitation inside sol-gel silica optical fiber preforms
Auteur(s) :
Chahadih, A. [Auteur]
Laboratoire de Physique des Lasers, Atomes et Molécules - UMR 8523 [PhLAM]
El Hamzaoui, Hicham [Auteur]
Laboratoire de Physique des Lasers, Atomes et Molécules - UMR 8523 [PhLAM]
Cristini-Robbe, Odile [Auteur]
Laboratoire de Physique des Lasers, Atomes et Molécules - UMR 8523 [PhLAM]
Bigot, Laurent [Auteur]
Laboratoire de Physique des Lasers, Atomes et Molécules - UMR 8523 [PhLAM]
Bernard, Remy [Auteur]
Laboratoire de Physique des Lasers, Atomes et Molécules - UMR 8523 [PhLAM]
Kinowski, Christophe [Auteur]
Laboratoire de Physique des Lasers, Atomes et Molécules - UMR 8523 [PhLAM]
Bouazaoui, Mohamed [Auteur]
Laboratoire de Physique des Lasers, Atomes et Molécules - UMR 8523 [PhLAM]
CAPOEN, Bruno [Auteur]
Laboratoire de Physique des Lasers, Atomes et Molécules - UMR 8523 [PhLAM]
Laboratoire de Physique des Lasers, Atomes et Molécules - UMR 8523 [PhLAM]
El Hamzaoui, Hicham [Auteur]
Laboratoire de Physique des Lasers, Atomes et Molécules - UMR 8523 [PhLAM]
Cristini-Robbe, Odile [Auteur]
Laboratoire de Physique des Lasers, Atomes et Molécules - UMR 8523 [PhLAM]
Bigot, Laurent [Auteur]
Laboratoire de Physique des Lasers, Atomes et Molécules - UMR 8523 [PhLAM]
Bernard, Remy [Auteur]
Laboratoire de Physique des Lasers, Atomes et Molécules - UMR 8523 [PhLAM]
Kinowski, Christophe [Auteur]
Laboratoire de Physique des Lasers, Atomes et Molécules - UMR 8523 [PhLAM]
Bouazaoui, Mohamed [Auteur]
Laboratoire de Physique des Lasers, Atomes et Molécules - UMR 8523 [PhLAM]
CAPOEN, Bruno [Auteur]
Laboratoire de Physique des Lasers, Atomes et Molécules - UMR 8523 [PhLAM]
Titre de la revue :
Nanoscale Research Letters
Pagination :
487
Éditeur :
SpringerOpen
Date de publication :
2012-08-31
ISSN :
1931-7573
Mot(s)-clé(s) :
copper nanoparticles
silver nanoparticles
surface plasmon resonance
sol-gel process
dense silica preforms
silver nanoparticles
surface plasmon resonance
sol-gel process
dense silica preforms
Discipline(s) HAL :
Physique [physics]/Physique [physics]/Optique [physics.optics]
Résumé en anglais : [en]
Ionic copper- or silver-doped dense silica rods have been prepared by sintering sol-gel porous silica xerogels doped with ionic precursors. The precipitation of Cu or Ag nanoparticles was achieved by heat treatment under ...
Lire la suite >Ionic copper- or silver-doped dense silica rods have been prepared by sintering sol-gel porous silica xerogels doped with ionic precursors. The precipitation of Cu or Ag nanoparticles was achieved by heat treatment under hydrogen followed by annealing under air atmosphere. The surface plasmon resonance bands of copper and silver nanoparticles have been clearly observed in the absorption spectra. The spectral positions of these bands were found to depend slightly on the particle size, which could be tuned by varying the annealing conditions. Hence, transmission electron microscopy showed the formation of spherical copper nanoparticles with diameters in the range of 3.3 to 5.6 nm. On the other hand, in the case of silver, both spherical nanoparticles with diameters in the range of 3 to 6 nm and nano-rods were obtained.Lire moins >
Lire la suite >Ionic copper- or silver-doped dense silica rods have been prepared by sintering sol-gel porous silica xerogels doped with ionic precursors. The precipitation of Cu or Ag nanoparticles was achieved by heat treatment under hydrogen followed by annealing under air atmosphere. The surface plasmon resonance bands of copper and silver nanoparticles have been clearly observed in the absorption spectra. The spectral positions of these bands were found to depend slightly on the particle size, which could be tuned by varying the annealing conditions. Hence, transmission electron microscopy showed the formation of spherical copper nanoparticles with diameters in the range of 3.3 to 5.6 nm. On the other hand, in the case of silver, both spherical nanoparticles with diameters in the range of 3 to 6 nm and nano-rods were obtained.Lire moins >
Langue :
Anglais
Vulgarisation :
Non
Projet ANR :
Source :
Fichiers
- https://hal.archives-ouvertes.fr/hal-00880321/document
- Accès libre
- Accéder au document
- https://nanoscalereslett.springeropen.com/track/pdf/10.1186/1556-276X-7-487
- Accès libre
- Accéder au document
- https://hal.archives-ouvertes.fr/hal-00880321/document
- Accès libre
- Accéder au document
- https://hal.archives-ouvertes.fr/hal-00880321/document
- Accès libre
- Accéder au document
- document
- Accès libre
- Accéder au document
- H2-induced_Cu_and_Ag_NP_-_NRL2012_-_Abdallah.pdf
- Accès libre
- Accéder au document