Solid-state 3D micro-supercapacitors based on ionogel electrolyte: Influence of adding lithium and sodium salts to the ionic liquid
Auteur(s) :
Guillemin, Thibaud [Auteur]
Douard, Camille [Auteur]
Réseau sur le stockage électrochimique de l'énergie [RS2E]
Institut des Matériaux de Nantes Jean Rouxel [IMN]
Robert, Kévin [Auteur]
Réseau sur le stockage électrochimique de l'énergie [RS2E]
Circuits Systèmes Applications des Micro-ondes - IEMN [CSAM - IEMN ]
Institut d’Électronique, de Microélectronique et de Nanotechnologie - UMR 8520 [IEMN]
Asbani, Bouchra [Auteur]
Laboratoire de Physique de la Matière Condensée - UR UPJV 2081 [LPMC]
Lethien, Christophe [Auteur correspondant]
Réseau sur le stockage électrochimique de l'énergie [RS2E]
Circuits Systèmes Applications des Micro-ondes - IEMN [CSAM - IEMN ]
Institut d’Électronique, de Microélectronique et de Nanotechnologie - UMR 8520 [IEMN]
Brousse, Thierry [Auteur correspondant]
Réseau sur le stockage électrochimique de l'énergie [RS2E]
Institut des Matériaux de Nantes Jean Rouxel [IMN]
Le Bideau, Jean [Auteur correspondant]
Institut des Matériaux de Nantes Jean Rouxel [IMN]
Douard, Camille [Auteur]
Réseau sur le stockage électrochimique de l'énergie [RS2E]
Institut des Matériaux de Nantes Jean Rouxel [IMN]
Robert, Kévin [Auteur]
Réseau sur le stockage électrochimique de l'énergie [RS2E]
Circuits Systèmes Applications des Micro-ondes - IEMN [CSAM - IEMN ]
Institut d’Électronique, de Microélectronique et de Nanotechnologie - UMR 8520 [IEMN]
Asbani, Bouchra [Auteur]
Laboratoire de Physique de la Matière Condensée - UR UPJV 2081 [LPMC]
Lethien, Christophe [Auteur correspondant]
Réseau sur le stockage électrochimique de l'énergie [RS2E]
Circuits Systèmes Applications des Micro-ondes - IEMN [CSAM - IEMN ]
Institut d’Électronique, de Microélectronique et de Nanotechnologie - UMR 8520 [IEMN]
Brousse, Thierry [Auteur correspondant]
Réseau sur le stockage électrochimique de l'énergie [RS2E]
Institut des Matériaux de Nantes Jean Rouxel [IMN]
Le Bideau, Jean [Auteur correspondant]
Institut des Matériaux de Nantes Jean Rouxel [IMN]
Titre de la revue :
Energy Storage Materials
Pagination :
606-617
Éditeur :
Elsevier
Date de publication :
2022-09
ISSN :
2405-8297
Mot(s)-clé(s) en anglais :
Microsupercapacitor
Interdigitated-3D-scaffold
MnO2
ionogel
Li-Na
Interdigitated-3D-scaffold
MnO2
ionogel
Li-Na
Discipline(s) HAL :
Sciences de l'ingénieur [physics]
Résumé en anglais : [en]
The ever-increasing interest in miniaturized Internet of Things devices and embedded electronics has given rise to a host of inquiries surrounding the need for safe, high performance energy storage devices. Solid-state 3D ...
Lire la suite >The ever-increasing interest in miniaturized Internet of Things devices and embedded electronics has given rise to a host of inquiries surrounding the need for safe, high performance energy storage devices. Solid-state 3D micro-supercapacitors based on ionogels provide a promising response to many of these pressing questions. Herein, leakage-free solid-state-like 3D micro-supercapacitors incorporating lithium and sodium salts added to 1-Ethyl-3-methylimidazolium bis(trifluoromethanesulfonyl)imide-based ionogels were investigated. The resulting micro-supercapacitors containing these lithium and sodium ions displayed energy densities of 10.2 and 9.5 µWh.cm−2 at power densities of 1.1 and 1.0 mW.cm−2, respectively. In those devoid of these alkaline ions, however, the energy density reached a mere 3 µWh.cm−2 at the same power density, thereby validating the proposed strategy. The 3D interdigitated MnO2 // MnO2 micro-supercapacitors were cycled 50 000 times at 1.75 mA.cm−2 with good capacitance retention (∼ 85 %). While performing under high temperatures (100°C), there was no evidence of electrolyte degradation, capacitance fading or electrolyte leakage.Lire moins >
Lire la suite >The ever-increasing interest in miniaturized Internet of Things devices and embedded electronics has given rise to a host of inquiries surrounding the need for safe, high performance energy storage devices. Solid-state 3D micro-supercapacitors based on ionogels provide a promising response to many of these pressing questions. Herein, leakage-free solid-state-like 3D micro-supercapacitors incorporating lithium and sodium salts added to 1-Ethyl-3-methylimidazolium bis(trifluoromethanesulfonyl)imide-based ionogels were investigated. The resulting micro-supercapacitors containing these lithium and sodium ions displayed energy densities of 10.2 and 9.5 µWh.cm−2 at power densities of 1.1 and 1.0 mW.cm−2, respectively. In those devoid of these alkaline ions, however, the energy density reached a mere 3 µWh.cm−2 at the same power density, thereby validating the proposed strategy. The 3D interdigitated MnO2 // MnO2 micro-supercapacitors were cycled 50 000 times at 1.75 mA.cm−2 with good capacitance retention (∼ 85 %). While performing under high temperatures (100°C), there was no evidence of electrolyte degradation, capacitance fading or electrolyte leakage.Lire moins >
Langue :
Anglais
Vulgarisation :
Non
Projet ANR :
Source :