Titre :

Influence of fiber-like nanofillers on the rheological, mechanical, thermal and fire properties of polypropylene: An application to multifilament yarn

Auteur(s) :

Vargas, Junior [Auteur]
Sciences Cognitives et Sciences Affectives (SCALab) - UMR 9193
Orozco, Víctor H. [Auteur]
Universidad de Antioquia = University of Antioquia [Medellín, Colombia]
Génie des Matériaux Textiles - ULR 2461 [GEMTEX]
Rault, François [Auteur]
Génie des Matériaux Textiles - ULR 2461 [GEMTEX]
Giraud, Stephane [Auteur]
Génie des Matériaux Textiles - ULR 2461 [GEMTEX]
Devaux, Éric [Auteur]
Génie des Matériaux Textiles - ULR 2461 [GEMTEX]
López, Betty L. [Auteur]
Universidad de Antioquia = University of Antioquia [Medellín, Colombia]

Titre de la revue :

Composites Part A: Applied Science and Manufacturing

Nom court de la revue :

Composites Part A: Applied Science and Manufacturing

Numéro :

41

Pagination :

1797-1806

Éditeur :

Elsevier BV

Date de publication :

2010-12

ISSN :

1359-835X

Discipline(s) HAL :

Sciences de l'ingénieur [physics]

Résumé en anglais : [en]

Polypropylene and polypropylene grafted maleic anhydride based composites with modified and non-modified carbon nanotubes and sepiolite were prepared by melt extrusion. Their thermal, rheological, and dynamic mechanical ...
Lire la suite >Polypropylene and polypropylene grafted maleic anhydride based composites with modified and non-modified carbon nanotubes and sepiolite were prepared by melt extrusion. Their thermal, rheological, and dynamic mechanical properties were evaluated. Multifilament yarns were obtained from the composites by spin-drawing process and their mechanical properties were measured. Knitted fabrics from the multifilament yarns were characterized by cone calorimetry. The best interaction was obtained for polypropylene/carbon nanotubes and polypropylene/polypropylene grafted maleic anhydride/sepiolite composites, as was confirmed by the increasing on the elastic modulus and thermal resistance. Nanofillers changed the thermal decomposition profiles compared to bare polypropylene. Knitted structures containing sepiolite decrease the maximum of heat release rate in comparison with unfilled samples.Lire moins >

Langue :

Anglais

Comité de lecture :

Oui

Audience :

Internationale

Vulgarisation :

Non

Établissement(s) :

Université de Lille
ENSAIT
Junia HEI

Collections :

• Génie des matériaux textiles (GEMTEX) - ULR 2641

Équipe(s) de recherche :

Multifunctional Textiles and Processes

Date de dépôt :

2025-03-18T15:09:54Z
2025-03-19T10:15:34Z