Effect of Zirconium and Cerium Loadings on Aerogel Pd-Based Catalysts for Methane Combustion

Auteur(s) :

Sadouki, Khouloud [Auteur]
Université de Tunis El Manar [UTM]
Fessi, Shemseddine [Auteur]
Université de Tunis El Manar [UTM]
Ksibi, Zouhaier [Auteur]
Université de Tunis El Manar [UTM]
Capron, Mickael [Auteur]
Unité de Catalyse et Chimie du Solide - UMR 8181 [UCCS]
Unité de Catalyse et Chimie du Solide (UCCS) - UMR 8181
Dumeignil, Franck [Auteur]
Unité de Catalyse et Chimie du Solide (UCCS) - UMR 8181
Unité de Catalyse et Chimie du Solide - UMR 8181 [UCCS]
Ghorbel, Abdelhamid [Auteur]
Université de Tunis El Manar [UTM]

Titre de la revue :

Advances in Materials Physics and Chemistry

Numéro :

8

Pagination :

105-119

Date de publication :

2018

Discipline(s) HAL :

Chimie/Catalyse

Résumé en anglais : [en]

Aerogel Pd/(Ce0.33Zr0.66O2)SiO2 catalysts (CeZry) were prepared with variable Ce and Zr loadings (molar ratio Ce/Zr = 1/2) by combining sol-gel and impregnation methods. First, N2-physisorption was used to investigate the ...
Lire la suite >Aerogel Pd/(Ce0.33Zr0.66O2)SiO2 catalysts (CeZry) were prepared with variable Ce and Zr loadings (molar ratio Ce/Zr = 1/2) by combining sol-gel and impregnation methods. First, N2-physisorption was used to investigate the texture evolution. Then, H2-chimisorption and TEM were performed to study the effect on particle dispersion. After, TPR was used to determine the catalyst reducibility. Furthermore, XPS characterization was done to identify the palladium oxidation state and to evaluate the Pd-support interaction. Finally, the prepared catalysts were tested in methane combustion to assess their catalytic activity. The obtained results showed that, when the Zr and Ce loadings are varied between 0% and 8% and between 0% and 6% respectively, the BET surface area was increased from 615 to 744 m2/g, the porosity diameter from 45.7 to 83.6 Å, the Pd particle diameter from 5.2 to 7.0 nm, the CeO2 and ZrO2 particle size from 0 to 68 nm, the reduction temperature shift reached 16°C, the Pd binding energy shift attained 0.6 eV, but an optimum amounts of Zr (4 wt.%) and Ce (3 wt.%) are needed to maximize the PdO reducibility and to enhance the catalytic activity. In effect, 100% conversion of methane was reached at around 415°C on the CeZr4 catalyst.Lire moins >

Langue :

Anglais

Comité de lecture :

Oui

Audience :

Internationale

Vulgarisation :

Non

Établissement(s) :

ENSCL
CNRS
Centrale Lille
Univ. Artois
Université de Lille

Collections :

• Unité de Catalyse et Chimie du Solide (UCCS) - UMR 8181

Équipe(s) de recherche :

Valorisation des alcanes et de la biomasse (VAALBIO)

Date de dépôt :

2019-09-25T14:37:50Z
2020-09-24T13:12:48Z