Flame resistance of geopolymer foam coatings ...
Document type :
Article dans une revue scientifique: Article original
Permalink :
Title :
Flame resistance of geopolymer foam coatings for the fire protection of steel
Author(s) :
Sarazin, Johan [Auteur]
Unité Matériaux et Transformations (UMET) - UMR 8207
Davy, Catherine [Auteur]
Unité de Catalyse et Chimie du Solide - UMR 8181 [UCCS]
Bourbigot, Serge [Auteur]
Institut universitaire de France [IUF]
Unité Matériaux et Transformations - UMR 8207 [UMET]
Unité Matériaux et Transformations (UMET) - UMR 8207
Tricot, Grégory [Auteur]
Laboratoire Avancé de Spectroscopie pour les Intéractions la Réactivité et l'Environnement - UMR 8516 [LASIRE]
Laboratoire Avancé de Spectroscopie pour les Intéractions la Réactivité et l'Environnement (LASIRE) - UMR 8516
Hosdez, Jerome [Auteur]
Laboratoire de Mécanique Multiphysique Multiéchelle [LaMcube]
Unité de Mécanique de Lille (UML) - ULR 7512
Lambertin, David [Auteur]
Laboratoire d’étude des Ciments et Bitumes pour le Conditionnement [LCBC]
Fontaine, Gaelle [Auteur]
Unité Matériaux et Transformations - UMR 8207 [UMET]
Unité Matériaux et Transformations (UMET) - UMR 8207
Unité Matériaux et Transformations (UMET) - UMR 8207
Davy, Catherine [Auteur]
Unité de Catalyse et Chimie du Solide - UMR 8181 [UCCS]
Bourbigot, Serge [Auteur]
Institut universitaire de France [IUF]
Unité Matériaux et Transformations - UMR 8207 [UMET]
Unité Matériaux et Transformations (UMET) - UMR 8207
Tricot, Grégory [Auteur]
Laboratoire Avancé de Spectroscopie pour les Intéractions la Réactivité et l'Environnement - UMR 8516 [LASIRE]
Laboratoire Avancé de Spectroscopie pour les Intéractions la Réactivité et l'Environnement (LASIRE) - UMR 8516
Hosdez, Jerome [Auteur]
Laboratoire de Mécanique Multiphysique Multiéchelle [LaMcube]
Unité de Mécanique de Lille (UML) - ULR 7512
Lambertin, David [Auteur]
Laboratoire d’étude des Ciments et Bitumes pour le Conditionnement [LCBC]
Fontaine, Gaelle [Auteur]
Unité Matériaux et Transformations - UMR 8207 [UMET]
Unité Matériaux et Transformations (UMET) - UMR 8207
Journal title :
Composites Part B: Engineering
Volume number :
222
Pages :
109045
Publisher :
Elsevier BV
Publication date :
2021-10-01
ISSN :
1359-8368
English keyword(s) :
Temperature
Stability
Alkali activated cement
Silica fume
Refractory cement
Stability
Alkali activated cement
Silica fume
Refractory cement
HAL domain(s) :
Chimie/Matériaux
Chimie/Polymères
Chimie/Polymères
English abstract : [en]
This research investigates the fire resistance of novel geopolymer (GP) foams, based on alkali-activated metakaolin and silica fume (SF). Fresh GP foams are applied as coatings on steel plates. After one week curing, the ...
Show more >This research investigates the fire resistance of novel geopolymer (GP) foams, based on alkali-activated metakaolin and silica fume (SF). Fresh GP foams are applied as coatings on steel plates. After one week curing, the foams are subjected to a flame burn-through test. Changes in their physico-chemical properties are characterized before and after fire test, mainly with XRD, quantitative MAS NMR, electron probe micro-analysis, quantitative X ray micro-computed tomography and heat conductivity. Results show that GP foams are excellent thermal barriers, providing up to 251 °C less than for uncoated steel plate. Their porosity ranges between 25 and 81%, for typical pore sizes d50 from 0.5 to 3.0 mm 29Si MAS NMR shows that the proportion of GP cement only decreases from 60-68% to 53–58% after fire. SF expands and creates small pores in the coating, which is favorable to decrease heat conductivity by a factor of 2 whatever the foam.Show less >
Show more >This research investigates the fire resistance of novel geopolymer (GP) foams, based on alkali-activated metakaolin and silica fume (SF). Fresh GP foams are applied as coatings on steel plates. After one week curing, the foams are subjected to a flame burn-through test. Changes in their physico-chemical properties are characterized before and after fire test, mainly with XRD, quantitative MAS NMR, electron probe micro-analysis, quantitative X ray micro-computed tomography and heat conductivity. Results show that GP foams are excellent thermal barriers, providing up to 251 °C less than for uncoated steel plate. Their porosity ranges between 25 and 81%, for typical pore sizes d50 from 0.5 to 3.0 mm 29Si MAS NMR shows that the proportion of GP cement only decreases from 60-68% to 53–58% after fire. SF expands and creates small pores in the coating, which is favorable to decrease heat conductivity by a factor of 2 whatever the foam.Show less >
Language :
Anglais
Peer reviewed article :
Oui
Audience :
Internationale
Popular science :
Non
European Project :
Administrative institution(s) :
Université de Lille
CNRS
INRA
ENSCL
CNRS
INRA
ENSCL
Collections :
Research team(s) :
Ingénierie des Systèmes Polymères
Chimie, matériaux et procédés pour un nucléaire durable (CIMEND)
Propriétés magnéto structurales des matériaux (PMSM)
Chimie, matériaux et procédés pour un nucléaire durable (CIMEND)
Propriétés magnéto structurales des matériaux (PMSM)
Submission date :
2021-06-23T08:43:18Z
2021-06-28T08:36:30Z
2021-07-09T15:11:47Z
2021-06-28T08:36:30Z
2021-07-09T15:11:47Z
Files
- 2021 06 J COMP part B Proof .pdf
- Version soumise (preprint)
- Restricted access
- Access the document