Preparation of Glass Fabric/Poly(L-lactide) Composites by Thermoplastic Resin Transfer Molding

Auteur(s) :

Louisy, Elodie [Auteur]
Unité de Catalyse et Chimie du Solide - UMR 8181 [UCCS]
Samyn, Fabienne [Auteur]
Unité Matériaux et Transformations - UMR 8207 [UMET]
Bourbigot, Serge [Auteur]
Unité Matériaux et Transformations - UMR 8207 [UMET]
Fontaine, Gaelle [Auteur]
Laboratoire de structures et propriétés de l'état solide [LSPES]
Unité Matériaux et Transformations - UMR 8207 [UMET]
Ingénierie des Systèmes Polymères
Bonnet, Fanny [Auteur]
Unité Matériaux et Transformations - UMR 8207 [UMET]

Titre de la revue :

Polymers

Nom court de la revue :

Polymers

Numéro :

11

Pagination :

339

Éditeur :

MDPI AG

Date de publication :

2019-02-15

ISSN :

2073-4360

Discipline(s) HAL :

Chimie/Matériaux

Résumé en anglais : [en]

This study reports the first example of the production of polylactide composites prepared by Thermoplastic Resin Transfer Molding (T-RTM) via in situ bulk polymerization of l-lactide (l-LA) after injection in a closed mold ...
Lire la suite >This study reports the first example of the production of polylactide composites prepared by Thermoplastic Resin Transfer Molding (T-RTM) via in situ bulk polymerization of l-lactide (l-LA) after injection in a closed mold containing glass fabrics. Tin octoate Sn(Oct)2 was used as the catalyst and first evaluated at the lab-scale in the experimental conditions required in the tank and in the mold of the RTM device. The reactions were then upscaled in the RTM in the absence of reinforcement to ensure the feasibility of the process (transfer and polymerization). Finally, poly-l-lactide (PLLA)-based composites with glass fabrics as the reinforcement were obtained. The resulting PLLA matrices exhibited conversions up to 99% along with high molar masses of up to 78,000 g·mol−1 when the polymerization was carried out under dynamic vacuum (vacuum-assisted RTM, VARTM). Moreover, a good impregnation of the glass fabrics by the matrix was observed by optical microscopy.Lire moins >

Langue :

Anglais

Audience :

Non spécifiée

Projet Européen :

MULTI-CONCEPTUAL DESIGN OF FIRE BARRIER: A SYSTEMIC APPROACH

Établissement(s) :

Université de Lille
CNRS
INRA
ENSCL

Collections :

• Unité de Catalyse et Chimie du Solide (UCCS) - UMR 8181
• Unité Matériaux et Transformations (UMET) - UMR 8207

Équipe(s) de recherche :

Ingénierie des Systèmes Polymères
Méthodologie organométallique pour la catalyse homogène (MOCAH)

Date de dépôt :

2019-04-02T18:43:32Z
2019-04-03T09:57:48Z