Poly(L-lactide-co-ε-caprolactone)-matrix composites produced in one step by in situ polymerization in TP-RTM

Auteur(s) :

Campos, Bernard [Auteur]
Unité Matériaux et Transformations - UMR 8207 [UMET]
Unité Matériaux et Transformations (UMET) - UMR 8207
Fontaine, Gaelle [Auteur]
Unité Matériaux et Transformations - UMR 8207 [UMET]
Unité Matériaux et Transformations (UMET) - UMR 8207
Bourbigot, Serge [Auteur]
Unité Matériaux et Transformations - UMR 8207 [UMET]
Unité Matériaux et Transformations (UMET) - UMR 8207
Stoclet, Gregory [Auteur]
Unité Matériaux et Transformations - UMR 8207 [UMET]
Unité Matériaux et Transformations (UMET) - UMR 8207
Bonnet, Fanny [Auteur correspondant]
Unité Matériaux et Transformations - UMR 8207 [UMET]
Unité Matériaux et Transformations (UMET) - UMR 8207

Titre de la revue :

ACS Applied Polymer Materials

Date de publication :

2022-08

ISSN :

2637-6105

Mot(s)-clé(s) en anglais :

Polylactic acid
biocomposites
TP-RTM
caprolactone
thermoplastic copolymer matrix
glass fabrics

Discipline(s) HAL :

Chimie/Matériaux
Chimie/Polymères

Résumé en anglais : [en]

Poly(L-Lactide) (PLLA) is a semi-crystalline biopolymer of great interest due to its biosourced, biocompatible and compostable nature. However, its brittleness prevents its use in a wide range of applications. In order to ...
Lire la suite >Poly(L-Lactide) (PLLA) is a semi-crystalline biopolymer of great interest due to its biosourced, biocompatible and compostable nature. However, its brittleness prevents its use in a wide range of applications. In order to reinforce PLLA, it is often used in polymer blends or in composites. In this contribution, an unprecedented family of PLLA-based / glass fabrics composites with poly(L-lactide-co--caprolactone) statistical copolymers as the matrix is reported. These biocomposites were produced in one step synthesis by in situ copolymerization of L-lactide and caprolactone in Thermoplastic Resin Transfer Molding (TP-RTM) process. These materials display high matrix/fabrics wettability along with strong rubbery character.Lire moins >

Langue :

Anglais

Comité de lecture :

Oui

Audience :

Internationale

Vulgarisation :

Non

Établissement(s) :

Université de Lille
CNRS
INRAE
ENSCL

Collections :

• Unité Matériaux et Transformations (UMET) - UMR 8207

Équipe(s) de recherche :

Ingénierie des Systèmes Polymères

Date de dépôt :

2022-08-30T09:12:21Z
2022-08-30T09:30:47Z
2022-09-02T06:25:40Z
2022-10-04T21:40:56Z
2022-11-17T12:53:56Z