Surface-initiated reversible addition fragmentation chain transfer of fluoromonomers: an efficient tool to improve interfacial adhesion in piezoelectric composites
Author(s) :
Bouad, Vincent [Auteur]
Unité Matériaux et Transformations (UMET) - UMR 8207
Ohno, Kohji [Auteur]
Department of Material and Life Science, Graduate School of Engineering, Osaka University
Addad, Ahmed [Auteur]
Unité Matériaux et Transformations (UMET) - UMR 8207
Marin, Adeline [Auteur]
Unité Matériaux et Transformations (UMET) - UMR 8207
Donzel, Nicolas [Auteur]
Institut Charles Gerhardt Montpellier - Institut de Chimie Moléculaire et des Matériaux de Montpellier [ICGM ICMMM]
Barrau, Sophie [Auteur]
Unité Matériaux et Transformations (UMET) - UMR 8207
Lyskawa, Joel [Auteur]
Unité Matériaux et Transformations (UMET) - UMR 8207
Ladmiral, Vincent [Auteur]
Institut Charles Gerhardt Montpellier - Institut de Chimie Moléculaire et des Matériaux de Montpellier [ICGM ICMMM]
Unité Matériaux et Transformations (UMET) - UMR 8207
Ohno, Kohji [Auteur]
Department of Material and Life Science, Graduate School of Engineering, Osaka University
Addad, Ahmed [Auteur]
Unité Matériaux et Transformations (UMET) - UMR 8207
Marin, Adeline [Auteur]
Unité Matériaux et Transformations (UMET) - UMR 8207
Donzel, Nicolas [Auteur]
Institut Charles Gerhardt Montpellier - Institut de Chimie Moléculaire et des Matériaux de Montpellier [ICGM ICMMM]
Barrau, Sophie [Auteur]
Unité Matériaux et Transformations (UMET) - UMR 8207
Lyskawa, Joel [Auteur]
Unité Matériaux et Transformations (UMET) - UMR 8207
Ladmiral, Vincent [Auteur]
Institut Charles Gerhardt Montpellier - Institut de Chimie Moléculaire et des Matériaux de Montpellier [ICGM ICMMM]
Journal title :
Polymer Chemistry
Abbreviated title :
Polym. Chem.
Volume number :
13
Pages :
6061-6072
Publisher :
Royal Society of Chemistry (RSC)
Publication date :
2022-10-12
ISSN :
1759-9954
HAL domain(s) :
Chimie/Matériaux
Chimie/Polymères
Chimie/Polymères
English abstract : [en]
This article reports the surface-initiated Reversible Addition–Fragmentation chain Transfer polymerization (SI-RAFT) of trifluoroethylene (TrFE) and vinylidene fluoride (VDF) from barium titanate nanoparticles (BTO NPs) ...
Show more >This article reports the surface-initiated Reversible Addition–Fragmentation chain Transfer polymerization (SI-RAFT) of trifluoroethylene (TrFE) and vinylidene fluoride (VDF) from barium titanate nanoparticles (BTO NPs) for the preparation of piezoelectric composites. A new xanthate chain transfer agent (DOPA-XA) derived from O-ethyl-S-(1-methoxy-carbonyl) ethyldithiocarbonate and integrating a catechol moiety able to efficiently bind onto the BTO NP surface was synthesized, characterized via1H and 13C NMR spectroscopy and employed to mediate SI-RAFT polymerizations. This DOPA-XA was immobilized onto BTO NPs and the grafting efficiency was evaluated by TEM images and XPS measurements while the grafting density (Γ > 0.2 chains per nm2) was calculated using TGA and BET measurements. Poly(trifluoroethylene)- (PTrFE) and poly(vinylidene fluoride-co-trifluoroethylene)- (P(VDF-co-TrFE) functionalized BTO NPs were prepared by SI-RAFT polymerization and characterized by nuclear magnetic resonance (NMR), size exclusion chromatography (SEC), thermogravimetric analysis (TGA), transmission electron macroscopy (TEM) and X-ray photoelectron microscopy (XPS). Interestingly, polymer brushes featuring relatively low dispersities (Đ < 1.5) and high grafting densities (Γ > 0.2 chains per nm2) were obtained. Piezoelectric composite films were then prepared from these fluoropolymer-decorated BTO NPs by incorporation into a P(VDF-co-TrFE) matrix using the solvent casting method. The homogeneity of the NPs dispersion in the copolymer matrix was assessed by SEM and the direct piezoelectric response of the composites was recorded after polarization and compared with composites prepared from non-modified BTO NPs. The measured piezoelectric coefficients (d33) of all the composites were of the same order of magnitude (around −9 pC N−1). Finally, the interface between the NPs and the copolymer matrix was mechanically stressed by stretching. The SEM images of the composite fracture showed, in the case of nongrafted BTO NPs, the presence of cavities close to the NPs associated with a weak interfacial adhesion while, for fluoropolymers grafted BTO NPs, the interface with the copolymer matrix was cohesive. This study leads to innovative composites with a cohesive ceramic/polymer interface for piezoelectric applications.Show less >
Show more >This article reports the surface-initiated Reversible Addition–Fragmentation chain Transfer polymerization (SI-RAFT) of trifluoroethylene (TrFE) and vinylidene fluoride (VDF) from barium titanate nanoparticles (BTO NPs) for the preparation of piezoelectric composites. A new xanthate chain transfer agent (DOPA-XA) derived from O-ethyl-S-(1-methoxy-carbonyl) ethyldithiocarbonate and integrating a catechol moiety able to efficiently bind onto the BTO NP surface was synthesized, characterized via1H and 13C NMR spectroscopy and employed to mediate SI-RAFT polymerizations. This DOPA-XA was immobilized onto BTO NPs and the grafting efficiency was evaluated by TEM images and XPS measurements while the grafting density (Γ > 0.2 chains per nm2) was calculated using TGA and BET measurements. Poly(trifluoroethylene)- (PTrFE) and poly(vinylidene fluoride-co-trifluoroethylene)- (P(VDF-co-TrFE) functionalized BTO NPs were prepared by SI-RAFT polymerization and characterized by nuclear magnetic resonance (NMR), size exclusion chromatography (SEC), thermogravimetric analysis (TGA), transmission electron macroscopy (TEM) and X-ray photoelectron microscopy (XPS). Interestingly, polymer brushes featuring relatively low dispersities (Đ < 1.5) and high grafting densities (Γ > 0.2 chains per nm2) were obtained. Piezoelectric composite films were then prepared from these fluoropolymer-decorated BTO NPs by incorporation into a P(VDF-co-TrFE) matrix using the solvent casting method. The homogeneity of the NPs dispersion in the copolymer matrix was assessed by SEM and the direct piezoelectric response of the composites was recorded after polarization and compared with composites prepared from non-modified BTO NPs. The measured piezoelectric coefficients (d33) of all the composites were of the same order of magnitude (around −9 pC N−1). Finally, the interface between the NPs and the copolymer matrix was mechanically stressed by stretching. The SEM images of the composite fracture showed, in the case of nongrafted BTO NPs, the presence of cavities close to the NPs associated with a weak interfacial adhesion while, for fluoropolymers grafted BTO NPs, the interface with the copolymer matrix was cohesive. This study leads to innovative composites with a cohesive ceramic/polymer interface for piezoelectric applications.Show less >
Language :
Anglais
Audience :
Internationale
Popular science :
Non
ANR Project :
Administrative institution(s) :
Université de Lille
CNRS
INRAE
ENSCL
CNRS
INRAE
ENSCL
Collections :
Research team(s) :
Ingénierie des Systèmes Polymères
Submission date :
2022-11-01T13:19:20Z
2022-11-01T13:40:02Z
2022-11-04T09:44:48Z
2022-11-01T13:40:02Z
2022-11-04T09:44:48Z
Files
- d2py00825d.pdf
- Version éditeur
- Open access
- Access the document