Titre :

Nanostructured BaTi(1-x)Sn(x)O(3 )ferroelectric materials for electrocaloric applications and energy performance

Auteur(s) :

Benyoussef, M. [Auteur]
Mura, T. [Auteur]
Unité de Catalyse et Chimie du Solide - UMR 8181 [UCCS]
1066418|||UCCS Équipe Couches Minces & Nanomatériaux
Saitzek, Sebastien [Auteur]
UCCS Équipe Couches Minces & Nanomatériaux
Unité de Catalyse et Chimie du Solide (UCCS) - UMR 8181
Azrour, F. [Auteur]
Blach, Jean-Francois [Auteur]
UCCS Équipe Couches Minces & Nanomatériaux
Unité de Catalyse et Chimie du Solide (UCCS) - UMR 8181
Lahmar, A. [Auteur]
Gagou, Y. [Auteur]
El Marssi, M. [Auteur]
SAYEDE, Adlane [Auteur]
UCCS Équipe Couches Minces & Nanomatériaux
Unité de Catalyse et Chimie du Solide (UCCS) - UMR 8181
Jouiad, M. [Auteur]

Titre de la revue :

Current Applied Physics

Numéro :

38

Pagination :

59-66

Éditeur :

Elsevier

Date de publication :

2022-06-24

ISSN :

1567-1739

Mot(s)-clé(s) en anglais :

BaTi1-xSnxO3
Nanomaterials
Electrocaloric
Energy storage

Discipline(s) HAL :

Physique [physics]/Matière Condensée [cond-mat]
Chimie/Matériaux
Chimie/Chimie inorganique

Résumé en anglais : [en]

Nanostructured BaTi1-xSnxO3 (x = 0, 0.05 & 0.075) were successfully synthesized using the modified Pechini processing method. The phase purity and symmetry were examined by X-ray diffraction and Raman spectroscopy. Tetragonal ...
Lire la suite >Nanostructured BaTi1-xSnxO3 (x = 0, 0.05 & 0.075) were successfully synthesized using the modified Pechini processing method. The phase purity and symmetry were examined by X-ray diffraction and Raman spectroscopy. Tetragonal symmetry was obtained for BaTiO3 (BT) while orthorhombic symmetry for Sn doped BT. BT exhibits an up-shift of the Curie temperature towards high temperatures (TC = 139 °C). In contrast, a down-shift was recorded for Sn doped BT. Then, indirect electrocaloric (EC) adiabatic temperature change ΔT and the energy storage performances were determined based on ferroelectric hysteresis loops. Interestingly, large EC responsivity of ΔT/ΔE = 0.81 × 10−6 K m/V was obtained for the BT accompanied with a moderate stored energy of 23 mJ/cm3 but with a high energy efficiency of 67%. The incorporation of Sn in BT was found to broaden the EC responsivity and to improve the energy efficiency up to 90%, recorded for the 5% Sn doped BT.Lire moins >

Langue :

Anglais

Comité de lecture :

Oui

Audience :

Internationale

Vulgarisation :

Non

Établissement(s) :

Université de Lille
CNRS
Centrale Lille
ENSCL
Univ. Artois

Collections :

• Unité de Catalyse et Chimie du Solide (UCCS) - UMR 8181

Équipe(s) de recherche :

Couches minces & nanomatériaux (CMNM)

Date de dépôt :

2023-05-03T00:25:08Z
2023-05-12T10:39:17Z