Titre :

Preparation of a Novel Intumescent Flame Retardant Based on Supramolecular Interactions and Its Application in Polyamide 11

Auteur(s) :

Jin, Xiaodong [Auteur]
Sun, Jun [Auteur]
Zhang, Jessica Shiqing [Auteur]
Gu, Xiaoyu [Auteur]
Bourbigot, Serge [Auteur]
Unité Matériaux et Transformations - UMR 8207 [UMET]
Li, Hongfei [Auteur]
Tang, Wufei [Auteur]
Zhang, Sheng [Auteur]
Unité Matériaux et Transformations - UMR 8207 [UMET]

Titre de la revue :

ACS Applied Materials & Interfaces

Numéro :

9

Pagination :

24964-24975

Date de publication :

2017-05-21

Discipline(s) HAL :

Sciences de l'ingénieur [physics]/Matériaux
Sciences de l'ingénieur [physics]/Génie des procédés
Chimie/Matériaux
Chimie/Polymères

Résumé en anglais : [en]

The flammability and melt dripping of the widely used bio-based polyamide 11 (PA 11) have attracted much attention in the last decade, and they are still a big challenge for the fire science society. In this work, a novel ...
Lire la suite >The flammability and melt dripping of the widely used bio-based polyamide 11 (PA 11) have attracted much attention in the last decade, and they are still a big challenge for the fire science society. In this work, a novel single macromolecular intumescent flame retardant (AM-APP) that contains an acid source and a gas source was prepared by supramolecular reactions between melamine and p-aminobenzene sulfonic acid, followed by an ionic exchange with ammonium polyphosphate. The chemical structure of AM-APP was characterized by Fourier transform infrared (FTIR) spectroscopy, X-ray photoelectron spectroscopy, and scanning electron microscopy. AM-APP and TiO2 were then introduced into PA 11 by melt compounding to improve the fire resistance of the composite. The fire performance of PA 11 composites was evaluated by the limiting oxygen index (LOI), vertical burning (UL-94), and cone calorimetry tests. The results showed that the presence of 22% AM-APP and 3% TiO2 increased the LOI value from 22.2 to 29.2%, upgraded the UL-94 rating from no rating to V-0, completely eliminated melt dripping, and significantly decreased the peak heat release rate from 943.4 to 177.5 kW/m2. The thermal behaviors were investigated by thermogravimetric (TG) analysis and TG-FTIR. It is suggested that AM-APP produces an intumescent char structure and releases inert gases, whereas TiO2 may consolidate the char layers, leading to the improvement in the fire resistance of PA 11.Lire moins >

Langue :

Anglais

Audience :

Internationale

Vulgarisation :

Non

Établissement(s) :

Université de Lille
ENSCL
CNRS
INRA

Collections :

• Unité Matériaux et Transformations (UMET) - UMR 8207

Équipe(s) de recherche :

Ingénierie des Systèmes Polymères

Date de dépôt :

2019-05-16T17:21:32Z
2024-07-10T08:32:43Z