Titre :

Highly stable fluorine-free slippery liquid infused surfaces

Auteur(s) :

Vaillard, Anne-Sophie [Auteur]
Institut d’Électronique, de Microélectronique et de Nanotechnologie - UMR 8520 [IEMN]
Bio-Micro-Electro-Mechanical Systems - IEMN [BIOMEMS - IEMN]
Saget, Manon [Auteur]
Institut d’Électronique, de Microélectronique et de Nanotechnologie - UMR 8520 [IEMN]
Braud, Flavie [Auteur]
Centrale de Micro Nano Fabrication - IEMN [CMNF - IEMN]
Institut d’Électronique, de Microélectronique et de Nanotechnologie - UMR 8520 [IEMN]
Lippert, Marc [Auteur]
Laboratoire d'Automatique, de Mécanique et d'Informatique industrielles et Humaines - UMR 8201 [LAMIH]
Keirsbulck, Laurent [Auteur]
Laboratoire d'Automatique, de Mécanique et d'Informatique industrielles et Humaines - UMR 8201 [LAMIH]
Jimenez, Maude [Auteur]
Institut universitaire de France [IUF]
Unité Matériaux et Transformations - UMR 8207 [UMET]
Coffinier, Yannick [Auteur]
NanoBioInterfaces - IEMN [NBI - IEMN]
Institut d’Électronique, de Microélectronique et de Nanotechnologie - UMR 8520 [IEMN]
Thomy, Vincent [Auteur]
Institut d’Électronique, de Microélectronique et de Nanotechnologie - UMR 8520 [IEMN]
Bio-Micro-Electro-Mechanical Systems - IEMN [BIOMEMS - IEMN]

Titre de la revue :

Surfaces and Interfaces

Nom court de la revue :

Surfaces and Interfaces

Numéro :

42, Part A

Pagination :

103296

Éditeur :

Elsevier

Date de publication :

2023-11

ISSN :

2468-0230

Mot(s)-clé(s) en anglais :

polymer molding
lubricant retention
wind tunnel
fouling release
SLIS

Discipline(s) HAL :

Sciences de l'ingénieur [physics]/Micro et nanotechnologies/Microélectronique
Chimie/Polymères

Résumé en anglais : [en]

A promising Slippery Liquid Infused Surface (SLIS) has been developed, that is both easy-to-produce and environmentally friendly. Using a double replication method, a 200 µm-thick texturized cross-linked PDMS film was ...
Lire la suite >A promising Slippery Liquid Infused Surface (SLIS) has been developed, that is both easy-to-produce and environmentally friendly. Using a double replication method, a 200 µm-thick texturized cross-linked PDMS film was obtained, leading to a grid of micrometric hills and deep wells. A comparison between perfluoropolyether (PFPE) lubricant and silicone oil of different viscosities highlights the advantage of silicone oil, which penetrates the cross-linked PDMS matrix even at high viscosity. Chemical modification with OTS (octadecyltrichlorosilane) and introduction of secondary structures through plasma etching, increased the surface's shear resistance. As a result, stable sliding properties were maintained after hundreds of cycles of immersion in water and, more originally still after tests under wind blowing exposure up to 78 m/s. Furthermore, addition of water sprayed during wind blowing exposure allows partial fouling release of the surface.Lire moins >

Langue :

Anglais

Audience :

Internationale

Vulgarisation :

Non

Projet ANR :

Design de surfaces anti-encrassantes pour les industries agroalimentaires
Plateforme de traitement laser pour l'électronique flexible multifonctionnelle

Établissement(s) :

Université de Lille
CNRS
INRAE
ENSCL

Collections :

• Institut d'Électronique, de Microélectronique et de Nanotechnologie (IEMN) - UMR 8520
• Unité Matériaux et Transformations (UMET) - UMR 8207

Date de dépôt :

2024-07-04T15:01:19Z
2024-08-23T08:32:48Z