Titre :

Incorporation of antimony‐bearing mining wastes into clinker Portland raw feed: The difficulty of Sb analysis in calcium silicates

Auteur(s) :

Chedrewih, Migueli [Auteur]
Centre for Materials and Processes [CERI MP - IMT Nord Europe]
Laboratoire de Génie Civil et Géo-Environnement (LGCgE) - ULR 4515 [LGCgE]
Thiéry, Vincent [Auteur]
Ecole nationale supérieure Mines-Télécom Lille Douai [IMT Nord Europe]
Laboratoire de Génie Civil et Géo-Environnement (LGCgE) - ULR 4515 [LGCgE]
Gauthier, Arnaud [Auteur]
Laboratoire de Génie Civil et Géo-Environnement (LGCgE) - ULR 4515 [LGCgE]
Amin, Fouad [Auteur]

Titre de la revue :

Journal of Microscopy

Éditeur :

Wiley

Date de publication :

2023-09-14

ISSN :

0022-2720

Discipline(s) HAL :

Chimie/Matériaux

Résumé en anglais : [en]

Within the global trend to valorise various mineral wastes as substituents in Portland cement clinker raw feed, mining wastes are promising candidates. However, they might still contain high levels of metallic elements. ...
Lire la suite >Within the global trend to valorise various mineral wastes as substituents in Portland cement clinker raw feed, mining wastes are promising candidates. However, they might still contain high levels of metallic elements. Their fate in the kiln is not always understood as well as their incorporation within the various clinker's phases. This is especially the case for antimony. Its in situ microanalysis by the means of energy‐dispersive spectroscopy is tricky since several of its L lines (L α1 = 3604,72 eV, L α2 = 3595,32 eV) overlap with calcium lines (K α1 = 3691,68 eV, K α2 = 3688,09 eV). Hence, at low concentrations, it is not possible to visualise its characteristics peaks. Increasing the counting rate by increasing the acceleration current results in the generation of spurious sum peaks, rendering the analysis not viable. Wavelength dispersive spectroscopy (i.e. electron microprobe) allows a better spectral resolution and quantification of Sb in the clinker phases. In a Portland cement clinker doped with 1% of Sb‐bearing mining waste, the Sb 2 O 3 content in belite and alite is in the 0.2–0.4 wt.% range as well as for C 3 A; in C 4 AF the content is higher, from 1.4 wt.% to 2 wt.%. However, there are microstructural evidence that Sb forms blebs from less than 1 μm in diameter up to 10 μm, included in calcium silicates. Hence, its incorporation in the lattice of calcium silicates is dubious. However, for ferrites and aluminates there is no microstructural evidence for remaining Sb‐bearing phases, suggesting a direct incorporation in crystal lattices.Lire moins >

Langue :

Anglais

Comité de lecture :

Oui

Audience :

Internationale

Vulgarisation :

Non

Collections :

• Laboratoire Génie Civil et géo-Environnement (LGCgE) - ULR 4515

Source :

Harvested from HAL

Date de dépôt :

2025-02-26T09:13:44Z