Titre :

Effect of the Small Punch Test sample geometry on the Liquid Metal Embrittlement of Cu-30 wt% Zn by the eGaIn

Auteur(s) :

Ezequiel, Marco [Auteur]
Unité Matériaux et Transformations (UMET) - UMR 8207
Proriol Serre, Ingrid [Auteur]
Unité Matériaux et Transformations (UMET) - UMR 8207

Éditeur(s) ou directeur(s) scientifique(s) :

Pantelakis, S.
Lampeas, G.
Tserpes, K.

Titre de la manifestation scientifique :

6th International Virtual Conference of Engineering Against Failure

Ville :

En visio - Grèce

Pays :

Grèce

Date de début de la manifestation scientifique :

2021-06-23

Titre de la revue :

MATEC Web of Conferences

Nom court de la revue :

MATEC Web Conf.

Éditeur :

EDP Sciences

Date de publication :

2021

ISSN :

2261-236X

Discipline(s) HAL :

Chimie/Matériaux

Résumé en anglais : [en]

Liquid metal embrittlement (LME) is the embrittlement or the modification of the fracture behaviour of a metal or alloy when it undergoes plastic deformation while in contact with a liquid metal or liquid alloy. LME ...
Lire la suite >Liquid metal embrittlement (LME) is the embrittlement or the modification of the fracture behaviour of a metal or alloy when it undergoes plastic deformation while in contact with a liquid metal or liquid alloy. LME occurrence depends strongly on the properties of the metals involved and on the conditions of the mechanical stresses applied to the solid. The Small Punch Test (SPT) on flat specimens is very sensitive to identify the conditions of LME occurrence. Moreover, there are alternative SPT notched specimen geometries that have the potential to screen solid/liquid couples for sensibility to LME in different conditions. To study the apparition of the LME on an alpha brass with 30 wt% Zn in contact with the eGaIn (Ga-In eutectic), SPT at room temperature were carried out at different displacement rates and using three specimen types: the standard flat geometry and two notched geometries. While the flat specimens did not present LME, the presence of a notch and a high strain rate induced LME on the other specimen geometries. For these last specimens, the eGaIn modifies the SPT load-displacement curves at the crack propagation stage and changes the fracture to a partially ductile fracture followed by a brittle fracture.Lire moins >

Langue :

Anglais

Comité de lecture :

Oui

Audience :

Internationale

Vulgarisation :

Non

Projet ANR :

Fragilisation par les métaux liquides : phénomènes et prédiction – appliquée au système alliages de Cuivre / Ga-In

Établissement(s) :

Université de Lille
CNRS
INRA
ENSCL

Collections :

• Unité Matériaux et Transformations (UMET) - UMR 8207

Équipe(s) de recherche :

Métallurgie Physique et Génie des Matériaux

Date de dépôt :

2021-11-16T09:49:57Z
2021-11-19T10:05:42Z