Titre :

Cellulose conversion to glycols over DUT-8(Ni) derived nickel-tungsten/carbons: selectivity tuning.

Auteur(s) :

Boulos, Joseph [Auteur]
Unité de Catalyse et Chimie du Solide - UMR 8181 [UCCS]
Goc, Firat [Auteur]
Institut de recherches sur la catalyse et l'environnement de Lyon [IRCELYON]
Perret, Noémie [Auteur]
Institut de recherches sur la catalyse et l'environnement de Lyon [IRCELYON]
Rataboul, Franck [Auteur]
Institut de recherches sur la catalyse et l'environnement de Lyon [IRCELYON]
Marceau, Eric [Auteur]
Unité de Catalyse et Chimie du Solide - UMR 8181 [UCCS]
Dhainaut, Jeremy [Auteur]
Unité de Catalyse et Chimie du Solide - UMR 8181 [UCCS]
royer, sebastien [Auteur]
Unité de Catalyse et Chimie du Solide - UMR 8181 [UCCS]

Titre de la manifestation scientifique :

GECAT 2023

Ville :

Dunkerque

Pays :

France

Date de début de la manifestation scientifique :

2023-06-06

Discipline(s) HAL :

Chimie/Catalyse

Résumé en anglais : [en]

There have been various studies on the transformation of cellulose to low carbon polyols (C2,3), ethylene glycol (EG), propylene glycol (PG) and glycerol (Gly), which are prevailing intermediates in the manufacture of ...
Lire la suite >There have been various studies on the transformation of cellulose to low carbon polyols (C2,3), ethylene glycol (EG), propylene glycol (PG) and glycerol (Gly), which are prevailing intermediates in the manufacture of plastics, pharmaceuticals, food additives, and cosmetics, etc. Cellulose conversion to diols mainly involves 3 types of reactions: cellulose hydrolysis, retro-aldol condensation, and hydrogenation. For the formation of 1,2-PG, the sugar isomerization reaction is also involved. Using activated carbon-supported tungsten carbide (W2C/AC) catalysts, Zhang et al. obtained an EG yield of 76 % starting from cellulose [1]. Besides being a cheap non-noble metal-derived phase, a noteworthy advantage of tungsten carbide over other tungsten species (oxides and metal) is the preferential formation of EG among other polyols due to its Pt-like catalytic behavior. Yang et al. prepared Ni-W/C nanofiber catalysts, in situ fabricated through the pyrolysis of Ni, W-containing metal-organic framework fibers. A large productivity varying from 15.3 to 70.8 molEG.h-1.gW-1 was reported, which is two orders of magnitude higher than previously reported Ni-W-based catalysts [2]. Interestingly Sun et al. [3] showed the impact of the Sn phase and valence on the catalytic properties of bimetallic systems supported on activated carbon. When powder of metallic Sn was used with Ni/AC, a Ni-Sn alloy formed which promoted retro-aldol cleavage and hydrogenation, finally favoring EG production (58 %). When SnO was used, the catalyst promoted glucose isomerization, leading preferentially to PG (32 %). The above studies inspired our current work. A series of W and Ni-containing metal-organic frameworks were constructed by one-pot assembly of DUT-8(Ni) MOF precursors and Na2WO4·2H2O. A subsequent pyrolysis of the W@ DUT-8(Ni) materials at 700 °C under nitrogen produced nickel-tungsten/carbon catalysts. The following nomenclature was adopted for the resulting materials: NiW-l-x-C-N2; where x (nW/nNi) was set at 0.06, 0.12, 0.3, and 0.43, respectively. Figure 1 displays the catalytic results of the as-synthesized materials in the cellulose hydrogenolysis at 245 °C in a reaction time of 1 hour. Both materials with low (NiW-l-0.06-C-N2) and high (NiW-l-0.3-C-N2) W content were selective to EG (17 %). A remarkable yield switch to PG (36 %) was obtained at an average W loading (NiW-l-0.12-C-N2). The highest EG molar yield (25 %) was obtained over NiW-l-0.43-C-N2.Lire moins >

Langue :

Anglais

Comité de lecture :

Non

Audience :

Nationale

Vulgarisation :

Non

Établissement(s) :

Université de Lille
CNRS
Centrale Lille
ENSCL
Univ. Artois

Collections :

• Unité de Catalyse et Chimie du Solide (UCCS) - UMR 8181

Équipe(s) de recherche :

Matériaux pour la catalyse (MATCAT)

Date de dépôt :

2023-11-17T15:10:56Z
2023-11-17T15:24:14Z
2023-11-23T15:26:39Z
2023-11-23T15:30:32Z